Electrochemical polishing of titanium rod, titanium alloy rod and TC4 titanium rod

               
Update: 09-12-2020
               
Abst:

Titanium rod barrel burnishing is to grind the parts an […]

Titanium rod barrel burnishing is to grind the parts and abrasives in dilute acid or dilute alkali with emulsifier (or corrosion inhibitor) and follow the rotation of the drum to obtain a bright appearance. It is suitable for the disposal of small parts and parts that are difficult to polish and polish. The correct selection of roller burnishing standards can improve productivity and quality.
   1. The shape of the roller
  The shape of the roller includes a circle, a hexagon, an octagon, etc., among which a polygon is good for practicality. This is because the radii of the barrel wall from the axis are not equal, and there is a certain point of view, so the rolling parts are easy to change the position, the chance of collision with each other increases, the grinding is uniform, and the efficiency is high, which can shorten the rolling time.
  2, the scale of the roller
   Straight adjustment is 50mm-100mm, and the length varies with the number of grids. The length of the first pattern roller is 600-800mm; the second pattern is 800-1500mm. Usually the larger one is better. This is because the parts are subjected to high pressure and friction in the drum, so the amount of cutting is also increased. But for those parts that are afraid of being stressed and easily deformed, a small roller can be used and the length of the roller can be increased.
  1) Materials for drum
   The speed of the drum is directly related to the amount of scraping of the parts within a certain range, that is, the faster the speed, the greater the scraping of the metal surface. However, when the speed exceeds a certain upper limit, it drops instead. Because when the rotation speed is too fast, the centrifugal force of the parts in the drum increases, which reduces the friction. Usually it is appropriate to control at 45r/min.
  2) Abrasives and solutions for barrel polishing
  The abrasives for rolling include pumice, quartz, granite skin angle, shells, iron filings and ceramic chips. The size of the abrasive particles should be larger or smaller than each hole of the Cen part. The amount of content in the drum is also an important factor affecting the quality of the agricultural surface of the parts. The amount of people inside the drum is usually 70% of the drum volume. Regarding the heavier titanium parts or threaded parts, the load should be controlled at 80%-90%. The solution in the drum should be added to about 95% of the drum volume (note: when adding acidic solution to the drum, you should add enough water first, and then add acid to avoid corrosion of parts during the tumbling process, because of the time increase , The concentration of the built-in solution gradually decreases, and even loses its effect. Therefore, the concentration of the solution should be checked and replaced at intervals. The burn-in time should not be too long, otherwise the parts will be damaged. That is, use a brush to remove the surface of the parts Burr, terbium, remaining oil and corrosion sludge, etc., and make the parts have a certain luster. Be sure to point out that elastic, rigid or thin-walled parts should be taken out in time after the finishing of rolling, otherwise it will easily cause hydrogen seepage or local over corrosion .